The single-component polyurethane waterproof coating is a kind of high-polymer waterproof coating which is made of isocyanate and polyether as main material, matched with additives such as hybrid latent solid agent, plasticizer, etc. through high-temp dehydration and polymerization. When in use, the rubber waterproof film is coated on a waterproof base layer, and a tough, soft and seamless rubber waterproof film is formed on the surface of the base layer through a chemical reaction between the-NCO end group in the polyurethane prepolymer and moisture in the air.
The double-component polyurethane waterproof coating which is a double-component chemical reaction curing waterproof material, wherein the component A is an isocyanate-blocked prepolymer obtained by-condensation of polyether and isocyanate, and the component B is a colored liquid consisting of a plasticizer, a curing agent, a thickening agent, accelerator and a filler. When in use, the components A and B are uniformly mixed in accordance with a certain proportion, coated on the surface of a waterproof base layer, through cure under room temperature to form a rubber-shaped elastic coating film, thereby playing a waterproof role.
Scope of Application
It is suitable for waterproof construction of various civil and industrial buildings such as roof, basement, bathroom and swimming pool. It is more suitable for waterproof engineering of place with complicated shape and crisscrossed pipes.
Product features
● The polyurethane waterproof coating forms a seamless and complete elastic waterproof layer after curing, which improves the waterproof and impermeability of building engineering. The coating film has high strength and extensibility, with strong adaptability to base cracking or expansion.
● It shall be firmly bonded with the base course, and waterproof coating material and concrete, wood, metal, ceramic, asbestos tile, etc.
● The construction is simple and convenient. Polyurethane coating is a kind of waterproof coating for cold construction. During construction, it can be brushed on the waterproof base layer.
● It is easy to maintain. The original waterproof effect can still be achieved only by repairing the damaged part locally. It is time-saving, labor-saving and low in cost.
● It is environment-friendly product, with small odor and less impact and damage to people and environment, and an ideal substitute for tar polyurethane.
Single-component polyurethane waterproof coating
Serial No. |
Project |
Technical index |
|||||
I-type |
II-type |
III-type |
|||||
1 |
Solid content % ≥ |
85 |
|||||
2 |
Drying time |
Surface drying time h ≤ |
12 |
||||
Actual drying time h ≤ |
24 |
||||||
3 |
Tensile strength Mpa ≥ |
2.0 |
6.0 |
12.0 |
|||
4 |
Elongation at break % ≥ |
500 |
450 |
150 |
|||
5 |
Impermeability 0.3Mpa 30Min |
Water impermeability |
|||||
6 |
Low temperature bendability ℃ ≤ |
-35 |
|||||
7 |
Bond strength Mpa ≥ |
1.0 |
|||||
|
Leveling a |
No obvious teeth marks at 20 min |