P02 polymer cement (JS) waterproof coating is a green environment-friendly waterproof coating, which is recommended by the state for residential construction. The material is a double-component waterproof coating compounded by organic liquids and inorganic powders, with the double characteristics of high elasticity of the organic material and good durability of the inorganic material, and it can form a waterproof coating film with high strength and toughness after being coated.
Product features
It can be directly constructed on wet or dry base layer made of various materials, and the elevation shall not flow;
The coating has high strength, toughness, water resistance, weathering resistance and excellent durability;
Pigments can be added to form a colored coating;
Waterborne coating is non-toxic, tasteless, pollution-free and environment-friendly;
Simple construction, short construction period, construction on wet base, strong cohesive force;
The coating shall have certain air permeability, so that the waterproof layer will not bulge even if the base layer is wet.
Scope of Application
JS composite waterproof coating can be constructed on the basis of damp or dry masonry, mortar, concrete, metal, wood, hard plastic, glass, gypsum board, foam board, asphalt, rubber, SBS coiled material, APP coiled material, polyurethane, etc., new and old industrial and civil buildings (e. g.: house, wall, underground, tunnel, bridge, sink, reservoir, bathroom, kitchen, etc.) can be used.
Technical performance index (Implementation Standards GB/T23445-2009)
Serial No. |
Project |
Technical index |
||
I-type |
II-type |
III-type |
||
1 |
Solid content % ≥ |
70 |
70 |
70 |
2 |
Tensile strength No treatment Mpa ≥ |
1.2 |
1.8 |
1.8 |
3 |
Elongation at break No treatment % ≥ |
200 |
80 |
30 |
4 |
Low temperature flexible φ 10 mm stick |
No cracks of -10 ℃ |
* |
* |
5 |
Impermeability 0.3Mpa 30Min |
Water impermeability |
Water impermeability |
Water impermeability |
6 |
Bond strength of wet base surface Mpa ≥ |
0.5 |
0.7 |
1.0 |